Because aluminum alloy has a severe tendency to oxidize and inhale, and it is in direct contact with furnace gas or the outside atmosphere during the smelting process, if the control is not properly controlled during the smelting process, the aluminum alloy can easily absorb gas and form pores. The most common is a pinhole. Pinholes usually refer to the precipitation pores less than 1mm in the casting, which is mostly circular and unevenly distributed on the entire section of the casting, especially in the thick and large section of the casting and the parts where the cooling rate is small. According to the distribution and shape characteristics of precipitation pores in aluminum alloys, pinholes can be divided into three categories.
The production practice of aluminum alloy hardware die-casting has confirmed that the main gas component of the pores formed by the aluminum alloy due to inhalation is hydrogen, and there is no certain rule to follow. Pinhole phenomenon; materials are no exception, and aluminum alloys of various compositions are prone to pinholes.
In the process of die-casting mold processing, if the conditions are very bad, problems such as grinding damage, fatigue, breakage, and shape change are often prone to occur. Therefore, the materials for die-casting mold processing must meet various requirements to avoid the various question.
The requirements for the material of the deep drawing die require that the materials of the running parts of the die have excellent resistance to adhesion and adsorption, high wear resistance and hardness, corresponding strength and toughness characteristics, and relatively superior cutting processing characteristics, and heat treatment. The shape changes are relatively small.
The materials used for the running parts of the blanking die with relatively thin plates need to have high wear resistance and hardness properties. However, for the punching die with thicker plate, in addition to having high wear resistance and resistance to pressure yield point, in order to avoid die fracture or chipping, die casting must also have high fracture resistance, high flexural strength and toughness.
Die-casting molds are generally subjected to certain impact, vibration, friction, higher pressure and stretching during processing. Sometimes they need to be processed at higher temperatures, and the environment is very diverse. Therefore, the manufacturing material requirements for die-casting mold processing are very high, and the materials selected in different working environments are also different.
For more information about zinc die casting process,die casting design,die casting method, we are glad to answer for you.